6061铝材属热处理可强化合金，具有良好的可成型性、可焊接性、可机加工性能，同时具有中等强度，在退火后仍能维持较好的操作性.6061铝材的主要合金元素是镁与硅，并形成Mg2Si相。若含有一定量的锰与铬，可以中和铁的坏作用；有时还添加少量的铜或锌，以提高合金的强度，而又不使其抗蚀性有明显降低；导电材料中还有少量的铜，以抵销钛及铁对导电性的不良影响；锆或钛能细化晶粒与控制再结晶组织；为了改善可切削性能，可加入铅与铋。在Mg2Si固溶于铝中，使合金有人工时效硬化功能。[1]
6061铝材的主要合金元素是镁与硅，并形成Mg2Si相。若含有一定量的锰与铬，可以中和铁的坏作用；有时还添加少量的铜或锌，以提高合金的强度，而又不使其抗蚀性有明显降低；导电材料中还有少量的铜，以抵销钛及铁对导电性的不良影响；锆或钛能细化晶粒与控制再结晶组织；为了改善可切削性能，可加入铅与铋。在Mg2Si固溶于铝中，使合金有人工时效硬化功能。6061铝材中的主要合金元素为镁与硅，具有中等强度、良好的抗腐蚀性、可焊接性，氧化效果较好。
化学成分：
铜Cu :0.15～0.4 锰Mn :0.15 镁Mg :0.8～1.2 锌Zn :0.25 铬Cr :0.04～0.35 钛Ti :0.15 硅Si :0.4～0.8 铁Fe :0.7 铝Al :余量
力学性能：
6061的极限抗拉强度为124 MPa 受拉屈服强度 55.2 MPa 延伸率25.0 % 弹性系数68.9 GPa 弯曲极限强度228 MPa Bearing Yield Strength 103 MPa 泊松比0.330 疲劳强度 62.1 MPa
热处理工艺：
快速退火：加热温度350～410℃;随材料有效厚度的不同，保温时间在30～120min之间;空气或水冷。2）高温退火：加热温度350～500℃;成品厚度≥6mm时，保温时间为10～30min、<6mm时，热透为止;空气冷。3）低温退火：加热温度150～250℃;保温时间为2～3h;空气或水冷。 6061铝合金密度为0.0000028